Experiments / Batch 68
Batch 68 not OK
02.06.2026 ·
Mr. Mohan Yadav ·
also written as S 9076 · S 9076 #68 · BYK 9076
Application test
not OK
3 tests
Conclusion — verbatim from the source
“Results: Not OK (Gloss and Colour strength inferior).”
S 9076 #68 not ok.docx, main table
Nothing extracted for this section yet.
Reaction conditions (optimized)
other: Re-solubility tested in Ethyl Acetate + Toluene (50:50)
Sample unspecified sample
not OK
Ink application (Nitrocellulose)
| Parameter | Standard | S 9076 |
|---|---|---|
| Grinding (µm) | < 5 µm | < 5 µm |
| Colour Shade | Reference Std | As per Std |
| Transparency | Reference Std | Slightly opaque |
| Color Strength (%) | 100.00 | 98-99 |
| Viscosity (B4 Cup @26°C) | 29 s | 30 s |
| Adhesion (Tape Test) | Pass | Pass |
| Gloss @ 60° | 67.1 | 62.2 |
| Re-solubility (Rating) | 3 | 1 |
| Separation | No | No |
| Settling | No | No |
not OK
Ink application (Nitrocellulose)
| Parameter | Standard | S 9076 |
|---|---|---|
| Grinding (µm) | < 5 µm | < 5 µm |
| Colour Shade | Reference Std | Bluer |
| Transparency | Reference Std | Transparent |
| Color Strength (%) | 100.00 | 30-40 |
| Viscosity (B4 Cup @26°C) | 27 s | 29 s |
| Adhesion (Tape Test) | Pass | Pass |
| Gloss @ 60° | 8.8 | 7.9 |
| Re-solubility (Rating) | 3 | 5 |
| Separation | No | No |
| Settling | No | No |
not OK
Ink application (Nitrocellulose)
| Parameter | Standard | S 9076 |
|---|---|---|
| Grinding (µm) | < 5 µm | < 5 µm |
| Colour Shade | Reference Std | As per Std |
| Transparency | Reference Std | As per Std |
| Color Strength (%) | 100.00 | 100.00 |
| Viscosity (B4 Cup @26°C) | 32 s | 33 s |
| Adhesion (Tape Test) | Pass | Pass |
| Gloss @ 60° | 41.9 | 43.6 |
| Re-solubility (Rating) | 3 | 2 |
| Separation | No | No |
| Settling | No | No |
Test report photos
S 9076 #68 not ok.docx — 3 photos
Where this record comes from
S 9076 #68 not ok.docx
— application testing
Something wrong on this page? Record a correction
Your correction is permanent: it survives every re-extraction and the field can no longer be changed by the system.
Field-by-field provenance (4 fields) — for auditors
1 extraction fragments · merged 2026-08-25 · 0 human-validated fields
Fix a wrong or missing extraction side-by-side with the original:
qwen-extract--S_9076_#68_not_ok--S_9076_68
| Field | Source | Extractor | Conf. |
|---|---|---|---|
| date | S 9076 #68 not ok.docx docx, main table + Re-solubility pages | qwen-tasks/extract-fragment.md@unversioned | high |
| scientist | S 9076 #68 not ok.docx docx, main table + Re-solubility pages | qwen-tasks/extract-fragment.md@unversioned | high |
| samples[0] | S 9076 #68 not ok.docx docx, main table + Re-solubility pages | qwen-tasks/extract-fragment.md@unversioned | high |
| outcome | S 9076 #68 not ok.docx docx, main table + Re-solubility pages | qwen-tasks/extract-fragment.md@unversioned | high |
Raw record JSON
{
"record_id": "exp-9076-068",
"project": "9076",
"aliases": [
"S 9076",
"S 9076 #68",
"BYK 9076"
],
"provenance": {
"fragments": [
"qwen-extract--S_9076_#68_not_ok--S_9076_68"
],
"field_provenance": {
"date": {
"source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #68 not ok.docx",
"extractor": "qwen-tasks/extract-fragment.md",
"extractor_version": "unversioned",
"extracted_date": "",
"locator": "docx, main table + Re-solubility pages",
"human_checked": true
},
"scientist": {
"source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #68 not ok.docx",
"extractor": "qwen-tasks/extract-fragment.md",
"extractor_version": "unversioned",
"extracted_date": "",
"locator": "docx, main table + Re-solubility pages",
"human_checked": true
},
"samples[0]": {
"source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #68 not ok.docx",
"extractor": "qwen-tasks/extract-fragment.md",
"extractor_version": "unversioned",
"extracted_date": "",
"locator": "docx, main table + Re-solubility pages",
"human_checked": true
},
"outcome": {
"source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #68 not ok.docx",
"extractor": "qwen-tasks/extract-fragment.md",
"extractor_version": "unversioned",
"extracted_date": "",
"locator": "docx, main table + Re-solubility pages",
"human_checked": true
}
},
"last_merged": "2026-08-25"
},
"documents": [
{
"file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #68 not ok.docx",
"role": "application_test",
"link_basis": "alias match: S 9076",
"link_status": "rule"
}
],
"validation": {
"validated_fields": {},
"corrections_applied": []
},
"date": "02.06.2026",
"scientist": "Mr. Mohan Yadav",
"conditions": {
"other": "Re-solubility tested in Ethyl Acetate + Toluene (50:50)"
},
"samples": [
{
"alias": "S 9076",
"batch_no": "68",
"application_tests": [
{
"test": "Ink application",
"system": "Nitrocellulose",
"parameter": "Violet 23",
"vs_reference": {
"Grinding (µm)": {
"ref_standard": "< 5 µm",
"S 9076": "< 5 µm"
},
"Colour Shade": {
"ref_standard": "Reference Std",
"S 9076": "As per Std"
},
"Transparency": {
"ref_standard": "Reference Std",
"S 9076": "Slightly opaque"
},
"Color Strength (%)": {
"ref_standard": "100.00",
"S 9076": "98-99"
},
"Viscosity (B4 Cup @26°C)": {
"ref_standard": "29 s",
"S 9076": "30 s"
},
"Adhesion (Tape Test)": {
"ref_standard": "Pass",
"S 9076": "Pass"
},
"Gloss @ 60°": {
"ref_standard": "67.1",
"S 9076": "62.2"
},
"Re-solubility (Rating)": {
"ref_standard": "3",
"S 9076": "1"
},
"Separation": {
"ref_standard": "No",
"S 9076": "No"
},
"Settling": {
"ref_standard": "No",
"S 9076": "No"
}
},
"verdict": "not ok"
},
{
"test": "Ink application",
"system": "Nitrocellulose",
"parameter": "Violet 27",
"vs_reference": {
"Grinding (µm)": {
"ref_standard": "< 5 µm",
"S 9076": "< 5 µm"
},
"Colour Shade": {
"ref_standard": "Reference Std",
"S 9076": "Bluer"
},
"Transparency": {
"ref_standard": "Reference Std",
"S 9076": "Transparent"
},
"Color Strength (%)": {
"ref_standard": "100.00",
"S 9076": "30-40"
},
"Viscosity (B4 Cup @26°C)": {
"ref_standard": "27 s",
"S 9076": "29 s"
},
"Adhesion (Tape Test)": {
"ref_standard": "Pass",
"S 9076": "Pass"
},
"Gloss @ 60°": {
"ref_standard": "8.8",
"S 9076": "7.9"
},
"Re-solubility (Rating)": {
"ref_standard": "3",
"S 9076": "5"
},
"Separation": {
"ref_standard": "No",
"S 9076": "No"
},
"Settling": {
"ref_standard": "No",
"S 9076": "No"
}
},
"verdict": "not ok"
},
{
"test": "Ink application",
"system": "Nitrocellulose",
"parameter": "Carbon Black N 330",
"vs_reference": {
"Grinding (µm)": {
"ref_standard": "< 5 µm",
"S 9076": "< 5 µm"
},
"Colour Shade": {
"ref_standard": "Reference Std",
"S 9076": "As per Std"
},
"Transparency": {
"ref_standard": "Reference Std",
"S 9076": "As per Std"
},
"Color Strength (%)": {
"ref_standard": "100.00",
"S 9076": "100.00"
},
"Viscosity (B4 Cup @26°C)": {
"ref_standard": "32 s",
"S 9076": "33 s"
},
"Adhesion (Tape Test)": {
"ref_standard": "Pass",
"S 9076": "Pass"
},
"Gloss @ 60°": {
"ref_standard": "41.9",
"S 9076": "43.6"
},
"Re-solubility (Rating)": {
"ref_standard": "3",
"S 9076": "2"
},
"Separation": {
"ref_standard": "No",
"S 9076": "No"
},
"Settling": {
"ref_standard": "No",
"S 9076": "No"
}
},
"verdict": "not ok"
}
],
"sample_id": "unspecified sample"
}
],
"outcome": {
"status": "not ok",
"basis": "Results: Not OK (Gloss and Colour strength inferior).",
"citation": "S 9076 #68 not ok.docx, main table"
}
}