	FINE ORGANIC INDUSTRIES LTD
	TEST REPORT
Project No			Issued on	04.05.2026
Issued by			Completed on	05.05.2026
Representative		Nature of Sample	Ref Standard	Batch
Sample Name	S 9076	Nature of Sample	Liquid	Liquid
Batch No	65	Colour of sample	Ref Standard	Batch
Reference Standard	BYK 9076	Colour of sample	Amber	Amber
Ink Base – Nitrocellulose Polyurethane
Testing Parameter	Violet 23		Violet 27
Testing Parameter	Ref Standard	Finalux 108	Ref Standard	Finalux 108
Grinding (µm)	< 5 µm	< 5 µm	< 5 µm	< 5 µm
Colour Shade	Reference Std	As per Std	Reference Std	As per Std
Transparency	Reference Std	Opaque	Reference Std	As per Std
Color Strength (%)	100.00	98-99	100.00	94-95
Viscosity (B4 Cup@26°C)	21 s	29 s	19 s	21 s
Adhesion (Tape Test)	Pass	Pass	Pass	Pass
Gloss @ 60°	66.4	55.9	7.8	9.1
Re-solubility (Rating)	4	2	4	2
Separation	No	No	No	No
Settling	No	No	No	No
Rating: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent
Note: Re-solubility tested in Ethyl Acetate + Toluene (50:50).
Results: Not OK (Gloss and Re-solubility inferior).
Completed By: Mr. Mohan Yadav
Authorized By: Dr. Sachin Jagtap

**Re-solubility**

Photos embedded in S 9076 #65 not ok.docx — 2

Extracted values

… checked

Cited: document body (test report table) (highlighted). Compare with the original on the left. Press Enter to OK the highlighted value, or click OK / fix on any value. Experiment: exp-9076-065

date high04.05.2026 scientist Mr. Mohan Yadav (Completed By); Dr. Sachin Jagtap (Authorized By)

Samples high

unspecified sample

#	test	system	pigment	reference_standard	conditions	result	vs_reference	verdict	failure_reason
0	Ink Base - Nitrocellulose Polyurethane, Violet 23	Ink Base - Nitrocellulose Polyurethane	Violet 23	Finalux 108	B4 Cup @26°C	{"Grinding (µm)": "< 5 µm", "Colour Shade": "As per Std", "Transparency": "Opaque", "Color Strength (%)": "98-99", "Viscosity (B4 Cup @26°C)": "29 s", "Adhesion (Tape Test)": "Pass", "Gloss @ 60°": "55.9", "Re-solubility (Rating)": "2", "Separation": "No", "Settling": "No"}	{"Grinding (µm)": "< 5 µm", "Colour Shade": "Reference Std", "Transparency": "Opaque (vs Reference Std)", "Color Strength (%)": "98-99 (vs 100.00)", "Viscosity (B4 Cup @26°C)": "29 s (vs 21 s)", "Adhesion (Tape Test)": "Pass", "Gloss @ 60°": "55.9 (vs 66.4)", "Re-solubility (Rating)": "2 (vs 4)", "Separation": "No", "Settling": "No"}	not ok	Gloss and Re-solubility inferior
1	Ink Base - Nitrocellulose Polyurethane, Violet 27	Ink Base - Nitrocellulose Polyurethane	Violet 27	Finalux 108	B4 Cup @26°C	{"Grinding (µm)": "< 5 µm", "Colour Shade": "As per Std", "Transparency": "As per Std", "Color Strength (%)": "94-95", "Viscosity (B4 Cup @26°C)": "21 s", "Adhesion (Tape Test)": "Pass", "Gloss @ 60°": "9.1", "Re-solubility (Rating)": "2", "Separation": "No", "Settling": "No"}	{"Grinding (µm)": "< 5 µm", "Colour Shade": "Reference Std", "Transparency": "As per Std", "Color Strength (%)": "94-95 (vs 100.00)", "Viscosity (B4 Cup @26°C)": "21 s (vs 19 s)", "Adhesion (Tape Test)": "Pass", "Gloss @ 60°": "9.1 (vs 7.8)", "Re-solubility (Rating)": "2 (vs 4)", "Separation": "No", "Settling": "No"}	not ok	Gloss and Re-solubility inferior

Outcome high

statusnot ok basisResults: Not OK (Gloss and Re-solubility inferior). citationS 9076 #65 not ok.docx, test report table

More actions — correct a value · link · ignore

History (1)

Action	Field	Value	Date
verify			2026-08-21

Raw fragment JSON

{
  "fragment_id": "app-test--S_9076_65_not_ok",
  "source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #65 not ok.docx",
  "derived_from": "ocr/S 9076 #65 not ok/S 9076 #65 not ok.md",
  "locator": "document body (test report table)",
  "extractor": "qwen-tasks/extract-fragment.md",
  "target_aliases": [
    "S 9076",
    "BYK 9076",
    "65"
  ],
  "document_role": "application_test",
  "payload": {
    "date": "04.05.2026",
    "scientist": "Mr. Mohan Yadav (Completed By); Dr. Sachin Jagtap (Authorized By)",
    "samples": [
      {
        "sample_name": "S 9076",
        "batch_no": "65",
        "nature": "Liquid",
        "colour": "Amber",
        "reference_standard": "BYK 9076",
        "application_tests": [
          {
            "test": "Ink Base - Nitrocellulose Polyurethane, Violet 23",
            "system": "Ink Base - Nitrocellulose Polyurethane",
            "pigment": "Violet 23",
            "reference_standard": "Finalux 108",
            "conditions": "B4 Cup @26°C",
            "result": "{\"Grinding (µm)\": \"< 5 µm\", \"Colour Shade\": \"As per Std\", \"Transparency\": \"Opaque\", \"Color Strength (%)\": \"98-99\", \"Viscosity (B4 Cup @26°C)\": \"29 s\", \"Adhesion (Tape Test)\": \"Pass\", \"Gloss @ 60°\": \"55.9\", \"Re-solubility (Rating)\": \"2\", \"Separation\": \"No\", \"Settling\": \"No\"}",
            "vs_reference": "{\"Grinding (µm)\": \"< 5 µm\", \"Colour Shade\": \"Reference Std\", \"Transparency\": \"Opaque (vs Reference Std)\", \"Color Strength (%)\": \"98-99 (vs 100.00)\", \"Viscosity (B4 Cup @26°C)\": \"29 s (vs 21 s)\", \"Adhesion (Tape Test)\": \"Pass\", \"Gloss @ 60°\": \"55.9 (vs 66.4)\", \"Re-solubility (Rating)\": \"2 (vs 4)\", \"Separation\": \"No\", \"Settling\": \"No\"}",
            "verdict": "not ok",
            "failure_reason": "Gloss and Re-solubility inferior"
          },
          {
            "test": "Ink Base - Nitrocellulose Polyurethane, Violet 27",
            "system": "Ink Base - Nitrocellulose Polyurethane",
            "pigment": "Violet 27",
            "reference_standard": "Finalux 108",
            "conditions": "B4 Cup @26°C",
            "result": "{\"Grinding (µm)\": \"< 5 µm\", \"Colour Shade\": \"As per Std\", \"Transparency\": \"As per Std\", \"Color Strength (%)\": \"94-95\", \"Viscosity (B4 Cup @26°C)\": \"21 s\", \"Adhesion (Tape Test)\": \"Pass\", \"Gloss @ 60°\": \"9.1\", \"Re-solubility (Rating)\": \"2\", \"Separation\": \"No\", \"Settling\": \"No\"}",
            "vs_reference": "{\"Grinding (µm)\": \"< 5 µm\", \"Colour Shade\": \"Reference Std\", \"Transparency\": \"As per Std\", \"Color Strength (%)\": \"94-95 (vs 100.00)\", \"Viscosity (B4 Cup @26°C)\": \"21 s (vs 19 s)\", \"Adhesion (Tape Test)\": \"Pass\", \"Gloss @ 60°\": \"9.1 (vs 7.8)\", \"Re-solubility (Rating)\": \"2 (vs 4)\", \"Separation\": \"No\", \"Settling\": \"No\"}",
            "verdict": "not ok",
            "failure_reason": "Gloss and Re-solubility inferior"
          }
        ],
        "sample_id": "unspecified sample"
      }
    ],
    "conclusion": "Results: Not OK (Gloss and Re-solubility inferior).",
    "outcome": {
      "status": "not ok",
      "basis": "Results: Not OK (Gloss and Re-solubility inferior).",
      "citation": "S 9076 #65 not ok.docx, test report table"
    },
    "notes": "Re-solubility tested in Ethyl Acetate + Toluene (50:50). Rating scale: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent. Issued on 04.05.2026, completed on 05.05.2026."
  },
  "field_confidence": {
    "date": "high",
    "samples": "high",
    "conclusion": "high",
    "outcome": "high"
  }
}