  "fragment_id": "qwen-extract--s-9076-69-not-ok--s-9076-69",
  "source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #69 not ok.docx",
  "derived_from": "ocr/S 9076 #69 not ok/S 9076 #69 not ok.md",
  "locator": "full document (single page application test report)",
  "extractor": "qwen-tasks/extract-fragment.md",
  "target_aliases": [
    "S 9076",
    "S 9076 #69"
  ],
  "document_role": "application_test",
  "payload": {
    "date": "02.06.2026",
    "date_completed": "09.06.2026",
    "scientist": "Mr. Mohan Yadav",
    "aim": "Application testing of sample S 9076 (batch 69) against reference standard BYK 9076 as dispersing additive in Nitrocellulose ink resin base, in Violet 23, Violet 27, and Carbon Black N 330 ink systems.",
    "materials": [
      {
        "name": "S 9076 (Batch No 69)",
        "role": "unknown",
        "physical_appearance": "Yellow viscous liquid",
        "role_verbatim": "sample under test"
      },
      {
        "name": "BYK 9076",
        "role": "unknown",
        "physical_appearance": "Amber to yellow viscous liquid",
        "role_verbatim": "reference standard"
      }
    ],
    "conditions": {
      "ink_resin_base": "Nitrocellulose",
      "other": "Re-solubility tested in Ethyl Acetate + Toluene (50:50). Viscosity measured B4 Cup @26°C. Re-solubility rating scale: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent."
    },
    "samples": [
      {
        "sample_name": "S 9076",
        "batch": "69",
        "reference_standard": "BYK 9076",
        "application_tests": [
          {
            "test": "Application test (grinding, colour, transparency, color strength, viscosity, adhesion, gloss, re-solubility, separation, settling)",
            "system": "Nitrocellulose ink, Violet 23",
            "result": "Grinding (µm): Ref Standard < 5 µm, S 9076 < 5 µm; Colour Shade: Ref Standard Reference Std, S 9076 As per Std; Transparency: Ref Standard Reference Std, S 9076 Slightly opaque; Color Strength (%): Ref Standard 100.00, S 9076 98-99; Viscosity (B4 Cup @26°C): Ref Standard 29 s, S 9076 30 s; Adhesion (Tape Test): Ref Standard Pass, S 9076 Pass; Gloss @ 60°: Ref Standard 67.1, S 9076 64.2; Re-solubility (Rating): Ref Standard 3, S 9076 1; Separation: Ref Standard No, S 9076 No; Settling: Ref Standard No, S 9076 No",
            "vs_reference": "Colour shade as per standard; transparency slightly opaque vs reference; color strength 98-99 vs 100.00; re-solubility 1 (Fail) vs 3 (Average)"
          },
          {
            "test": "Application test (grinding, colour, transparency, color strength, viscosity, adhesion, gloss, re-solubility, separation, settling)",
            "system": "Nitrocellulose ink, Violet 27",
            "result": "Grinding (µm): Ref Standard < 5 µm, S 9076 < 5 µm; Colour Shade: Ref Standard Reference Std, S 9076 Bluer; Transparency: Ref Standard Reference Std, S 9076 Transparent; Color Strength (%): Ref Standard 100.00, S 9076 60-70; Viscosity (B4 Cup @26°C): Ref Standard 27 s, S 9076 28 s; Adhesion (Tape Test): Ref Standard Pass, S 9076 Pass; Gloss @ 60°: Ref Standard 8.8, S 9076 7.9; Re-solubility (Rating): Ref Standard 3, S 9076 18.5; Separation: Ref Standard No, S 9076 No; Settling: Ref Standard No, S 9076 No",
            "vs_reference": "Colour shade bluer; color strength 60-70 vs 100.00; gloss 7.9 vs 8.8; re-solubility value 18.5 (outside 1-5 rating scale, verbatim as printed) vs 3"
          },
          {
            "test": "Application test (grinding, colour, transparency, color strength, viscosity, adhesion, gloss, re-solubility, separation, settling)",
            "system": "Nitrocellulose ink, Carbon Black N 330",
            "result": "Grinding (µm): Ref Standard < 5 µm, S 9076 < 5 µm; Colour Shade: Ref Standard Reference Std, S 9076 As per Std; Transparency: Ref Standard Reference Std, S 9076 As per Std; Color Strength (%): Ref Standard 100.00, S 9076 100.00; Viscosity (B4 Cup @26°C): Ref Standard 32 s, S 9076 33 s; Adhesion (Tape Test): Ref Standard Pass, S 9076 Pass; Gloss @ 60°: Ref Standard 41.9, S 9076 45.4; Re-solubility (Rating): Ref Standard 3, S 9076 2; Separation: Ref Standard No, S 9076 No; Settling: Ref Standard No, S 9076 No",
            "vs_reference": "Matches reference on all parameters; re-solubility 2 (Poor) vs 3 (Average); gloss slightly higher (45.4 vs 41.9)"
          }
        ],
        "sample_id": "unspecified sample"
      }
    ],
    "observations": [
      "Physical appearance: Reference Standard BYK 9076 – Amber to yellow viscous liquid; S 9076 – Yellow viscous liquid.",
      "Violet 23: S 9076 slightly opaque, color strength 98-99 vs 100.00, re-solubility rating 1 (Fail) vs 3.",
      "Violet 27: S 9076 colour shade bluer, color strength 60-70 vs 100.00, re-solubility printed value 18.5 vs 3.",
      "Carbon Black N 330: S 9076 in line with reference on all printed parameters."
    ],
    "outcome": {
      "status": "not ok",
      "basis": "Results: Not OK (Gloss and Colour strength inferior).",
      "citation": "S 9076 #69 not ok.docx, application test report (Results row)"
    },
    "notes": "Violet 27 Re-solubility value for S 9076 is printed as '18.5', outside the stated 1-5 rating scale; kept verbatim per extraction rules (possible OCR/source typo, not corrected). Report issued by Mr. Satish Warghude, completed by Mr. Mohan Yadav, authorized by Dr. Sachin Jagtap."
  },
  "field_confidence": {
    "date": "high",
    "date_completed": "high",
    "scientist": "high",
    "aim": "medium",
    "materials": "high",
    "conditions": "high",
    "samples": "high",
    "observations": "high",
    "outcome": "high",
    "notes": "high"
  }
}