	FINE ORGANIC INDUSTRIES LTD
	TEST REPORT
Project No			Issued on	04.05.2026
Issued by			Completed on	05.05.2026
Representative		Nature of Sample	Ref Standard	Batch
Sample Name	S 9076	Nature of Sample	Liquid	Liquid
Batch No	64	Colour of sample	Ref Standard	Batch
Reference Standard	BYK 9076	Colour of sample	Amber	Yellow
Ink Base – Nitrocellulose Polyurethane
Testing Parameter	Violet 23		Violet 27
Testing Parameter	Ref Standard	Finalux 108	Ref Standard	Finalux 108
Grinding (µm)	< 5 µm	< 5 µm	< 5 µm	< 5 µm
Colour Shade	Reference Std	As per Std	Reference Std	As per Std
Transparency	Reference Std	Opaque	Reference Std	Opaque
Color Strength (%)	100.00	98-99	100.00	92-93
Viscosity (B4 Cup@26°C)	21 s	23 s	19 s	20 s
Adhesion (Tape Test)	Pass	Pass	Pass	Pass
Gloss @ 60°	66.4	55.6	7.8	8.9
Re-solubility (Rating)	4	2	4	2
Separation	No	No	No	No
Settling	No	No	No	No
Rating: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent
Note: Re-solubility tested in Ethyl Acetate + Toluene (50:50).
Results: Not OK (Gloss and Re-solubility inferior).
Completed By: Mr. Mohan Yadav
Authorized By: Dr. Sachin Jagtap

**Re-solubility**

Photos embedded in S 9076 #64 not ok.docx — 2

Extracted values

… checked

Cited: document (single page) (highlighted). Compare with the original on the left. Press Enter to OK the highlighted value, or click OK / fix on any value. Experiment: exp-9076-076

date high04.05.2026 scientist highMr. Mohan Yadav aim mediumApplication test of S 9076 Batch No 64 vs BYK 9076 in ink systems (Violet 23, Violet 27) in Nitrocellulose Polyurethane ink base

Materials high

#	name	role	role_verbatim
0	Ink Base – Nitrocellulose Polyurethane	unknown	ink base
1	Violet 23	unknown	colourant system
2	Violet 27	unknown	colourant system
3	Finalux 108	unknown	reference standard for both ink systems

Samples high

unspecified sample

#	test	system	reference	conditions	result	vs_reference
0	Application test in Ink Base – Nitrocellulose Polyurethane	Violet 23	BYK 9076 / Finalux 108	Re-solubility tested in Ethyl Acetate + Toluene (50:50); Viscosity B4 Cup @26°C; Gloss @ 60°	Grinding < 5 µm (Ref Std), Colour Shade As per Std, Transparency Opaque (vs Reference Std), Color Strength 98-99 (vs 100.00), Viscosity 23 s (vs 21 s), Adhesion Tape Test Pass, Gloss @ 60° 55.6 (vs 66.4), Re-solubility Rating 2 (vs 4), Separation No, Settling No	Gloss inferior (55.6 vs 66.4); Re-solubility inferior (rating 2 Poor vs 4 Good); Colour Strength 98-99 vs 100.00; Transparency Opaque vs Reference Std
1	Application test in Ink Base – Nitrocellulose Polyurethane	Violet 27	BYK 9076 / Finalux 108	Re-solubility tested in Ethyl Acetate + Toluene (50:50); Viscosity B4 Cup @26°C; Gloss @ 60°	Grinding < 5 µm (Ref Std), Colour Shade As per Std, Transparency Opaque (vs Reference Std), Color Strength 92-93 (vs 100.00), Viscosity 20 s (vs 19 s), Adhesion Tape Test Pass, Gloss @ 60° 8.9 (vs 7.8), Re-solubility Rating 2 (vs 4), Separation No, Settling No	Re-solubility inferior (rating 2 Poor vs 4 Good); Colour Strength 92-93 vs 100.00; Transparency Opaque vs Reference Std

Outcome high

statusnot ok basisResults: Not OK (Gloss and Re-solubility inferior). citationpdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #64 not ok.docx

More actions — correct a value · link · ignore

History (1)

Action	Field	Value	Date
link		exp-9076-076	2026-08-21

Raw fragment JSON

{
  "fragment_id": "qwen-extract--s-9076-64-not-ok--s-9076-64",
  "source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #64 not ok.docx",
  "derived_from": "ocr/S 9076 #64 not ok.md",
  "locator": "document (single page)",
  "extractor": "qwen-tasks/extract-fragment.md",
  "target_aliases": [
    "S 9076",
    "BYK 9076",
    "Finalux 108"
  ],
  "document_role": "application_test",
  "payload": {
    "date": "04.05.2026",
    "completed_on": "05.05.2026",
    "scientist": "Mr. Mohan Yadav",
    "authorized_by": "Dr. Sachin Jagtap",
    "sample": {
      "sample_name": "S 9076",
      "batch_no": "64",
      "nature_of_sample": "Liquid",
      "colour_of_sample": "Amber"
    },
    "reference_standard": {
      "name": "BYK 9076",
      "nature_of_sample": "Liquid",
      "colour_of_sample": "Yellow"
    },
    "aim": "Application test of S 9076 Batch No 64 vs BYK 9076 in ink systems (Violet 23, Violet 27) in Nitrocellulose Polyurethane ink base",
    "materials": [
      {
        "name": "Ink Base – Nitrocellulose Polyurethane",
        "role": "unknown",
        "role_verbatim": "ink base"
      },
      {
        "name": "Violet 23",
        "role": "unknown",
        "role_verbatim": "colourant system"
      },
      {
        "name": "Violet 27",
        "role": "unknown",
        "role_verbatim": "colourant system"
      },
      {
        "name": "Finalux 108",
        "role": "unknown",
        "role_verbatim": "reference standard for both ink systems"
      }
    ],
    "samples": [
      {
        "id": "S 9076 Batch No 64",
        "application_tests": [
          {
            "test": "Application test in Ink Base – Nitrocellulose Polyurethane",
            "system": "Violet 23",
            "reference": "BYK 9076 / Finalux 108",
            "conditions": "Re-solubility tested in Ethyl Acetate + Toluene (50:50); Viscosity B4 Cup @26°C; Gloss @ 60°",
            "result": "Grinding < 5 µm (Ref Std), Colour Shade As per Std, Transparency Opaque (vs Reference Std), Color Strength 98-99 (vs 100.00), Viscosity 23 s (vs 21 s), Adhesion Tape Test Pass, Gloss @ 60° 55.6 (vs 66.4), Re-solubility Rating 2 (vs 4), Separation No, Settling No",
            "vs_reference": "Gloss inferior (55.6 vs 66.4); Re-solubility inferior (rating 2 Poor vs 4 Good); Colour Strength 98-99 vs 100.00; Transparency Opaque vs Reference Std"
          },
          {
            "test": "Application test in Ink Base – Nitrocellulose Polyurethane",
            "system": "Violet 27",
            "reference": "BYK 9076 / Finalux 108",
            "conditions": "Re-solubility tested in Ethyl Acetate + Toluene (50:50); Viscosity B4 Cup @26°C; Gloss @ 60°",
            "result": "Grinding < 5 µm (Ref Std), Colour Shade As per Std, Transparency Opaque (vs Reference Std), Color Strength 92-93 (vs 100.00), Viscosity 20 s (vs 19 s), Adhesion Tape Test Pass, Gloss @ 60° 8.9 (vs 7.8), Re-solubility Rating 2 (vs 4), Separation No, Settling No",
            "vs_reference": "Re-solubility inferior (rating 2 Poor vs 4 Good); Colour Strength 92-93 vs 100.00; Transparency Opaque vs Reference Std"
          }
        ],
        "sample_id": "unspecified sample"
      }
    ],
    "rating_scale": "Rating: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent",
    "notes": "Note: Re-solubility tested in Ethyl Acetate + Toluene (50:50).",
    "conclusion": "Results: Not OK (Gloss and Re-solubility inferior).",
    "outcome": {
      "status": "not ok",
      "basis": "Results: Not OK (Gloss and Re-solubility inferior).",
      "citation": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #64 not ok.docx"
    }
  },
  "field_confidence": {
    "date": "high",
    "scientist": "high",
    "aim": "medium",
    "materials": "high",
    "samples": "high",
    "conclusion": "high",
    "outcome": "high"
  },
  "notes": "Issued by / Representative fields are blank in the source. Project No is blank."
}