FINE ORGANIC INDUSTRIES LTD
TEST REPORT
Project No Issued on 04.05.2026
Issued by Completed on 05.05.2026
Representative Nature of Sample Ref Standard Batch
Sample Name S 9076 Liquid Liquid
Batch No 63 Colour of sample Ref Standard Batch
Reference Standard BYK 9076 Amber Amber
Ink Base – Nitrocellulose Polyurethane
Testing Parameter Violet 23 Violet 27
Ref Standard Finalux 108 Ref Standard Finalux 108
Grinding (µm) < 5 µm < 5 µm < 5 µm < 5 µm
Colour Shade Reference Std As per Std Reference Std As per Std
Transparency Reference Std Opaque Reference Std Opaque
Color Strength (%) 100.00 98-99 100.00 100.00
Viscosity (B4 Cup@26°C) 21 s 22 s 19 s 20 s
Adhesion (Tape Test) Pass Pass Pass Pass
Gloss @ 60° 66.4 55.7 7.8 8.1
Re-solubility (Rating) 4 2 4 2
Separation No No No No
Settling No No No No
Rating: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent
Note: Re-solubility tested in Ethyl Acetate + Toluene (50:50).
Results: Not OK (Gloss and Re-solubility inferior).
Completed By: Mr. Mohan Yadav
Authorized By: Dr. Sachin Jagtap
**Re-solubility**
Photos embedded in S 9076 #63 not ok.docx — 2

Extracted values

… checked
Cited: docx table, single page (highlighted). Compare with the original on the left. Press Enter to OK the highlighted value, or click OK / fix on any value. Experiment: exp-9076-063
date high04.05.2026 issued; 05.05.2026 completed scientist highCompleted By: Mr. Mohan Yadav; Authorized By: Dr. Sachin Jagtap aim mediumApplication test report: S 9076 Batch No 63 vs Reference Standard BYK 9076 in Ink Base – Nitrocellulose Polyurethane (Finalux 108), shades Violet 23 and Violet 27

Samples high

unspecified sample
#testsystemconditionsresultvs_referenceverdictfailure_reason
0 Ink base evaluation Ink Base – Nitrocellulose Polyurethane, Finalux 108, Violet 23 Viscosity measured as B4 Cup @26°C; Gloss @ 60°; Re-solubility tested in Ethyl Acetate + Toluene (50:50) Grinding (µm): < 5 µm (Ref Standard < 5 µm); Colour Shade: As per Std (Ref Standard); Transparency: Opaque (Ref Standard); Color Strength (%): 98-99 (Ref Standard 100.00); Viscosity (B4 Cup @26°C): 22 s (Ref Standard 21 s); Adhesion (Tape Test): Pass (Ref Standard Pass); Gloss @ 60°: 55.7 (Ref Standard 66.4); Re-solubility (Rating): 2 (Ref Standard 4); Separation: No (Ref Standard No); Settling: No (Ref Standard No) Gloss and Re-solubility inferior to BYK 9076 not ok Gloss and Re-solubility inferior
1 Ink base evaluation Ink Base – Nitrocellulose Polyurethane, Finalux 108, Violet 27 Viscosity measured as B4 Cup @26°C; Gloss @ 60°; Re-solubility tested in Ethyl Acetate + Toluene (50:50) Grinding (µm): < 5 µm (Ref Standard < 5 µm); Colour Shade: As per Std (Ref Standard); Transparency: Opaque (Ref Standard); Color Strength (%): 100.00 (Ref Standard 100.00); Viscosity (B4 Cup @26°C): 20 s (Ref Standard 19 s); Adhesion (Tape Test): Pass (Ref Standard Pass); Gloss @ 60°: 8.1 (Ref Standard 7.8); Re-solubility (Rating): 2 (Ref Standard 4); Separation: No (Ref Standard No); Settling: No (Ref Standard No) Re-solubility inferior to BYK 9076 not ok Gloss and Re-solubility inferior

Outcome high

statusnot ok basisResults: Not OK (Gloss and Re-solubility inferior). citation[S 9076 #63 not ok.docx, section "Results"]
More actions — correct a value · link · ignore
Action Field path Corrected value Cause Note permanent — survives every re-run
History (1)
ActionFieldValueDate
verify 2026-08-21
Raw fragment JSON 
{
  "fragment_id": "qwen-extract--s-9076-63-not-ok--s-9076-63",
  "source_file": "pdf/9076 Data for Raven POC project/Application tetsing Report/S 9076 #63 not ok.docx",
  "derived_from": "ocr/S 9076 #63 not ok.md",
  "locator": "docx table, single page",
  "extractor": "qwen-tasks/extract-fragment.md",
  "target_aliases": [
    "S 9076",
    "Batch No 63",
    "BYK 9076"
  ],
  "document_role": "application_test",
  "payload": {
    "date": "04.05.2026 issued; 05.05.2026 completed",
    "scientist": "Completed By: Mr. Mohan Yadav; Authorized By: Dr. Sachin Jagtap",
    "aim": "Application test report: S 9076 Batch No 63 vs Reference Standard BYK 9076 in Ink Base – Nitrocellulose Polyurethane (Finalux 108), shades Violet 23 and Violet 27",
    "samples": [
      {
        "alias": "S 9076 Batch No 63",
        "nature": "Liquid",
        "colour": "Amber",
        "reference_standard": "BYK 9076",
        "application_tests": [
          {
            "test": "Ink base evaluation",
            "system": "Ink Base – Nitrocellulose Polyurethane, Finalux 108, Violet 23",
            "conditions": "Viscosity measured as B4 Cup @26°C; Gloss @ 60°; Re-solubility tested in Ethyl Acetate + Toluene (50:50)",
            "result": "Grinding (µm): < 5 µm (Ref Standard < 5 µm); Colour Shade: As per Std (Ref Standard); Transparency: Opaque (Ref Standard); Color Strength (%): 98-99 (Ref Standard 100.00); Viscosity (B4 Cup @26°C): 22 s (Ref Standard 21 s); Adhesion (Tape Test): Pass (Ref Standard Pass); Gloss @ 60°: 55.7 (Ref Standard 66.4); Re-solubility (Rating): 2 (Ref Standard 4); Separation: No (Ref Standard No); Settling: No (Ref Standard No)",
            "vs_reference": "Gloss and Re-solubility inferior to BYK 9076",
            "verdict": "not ok",
            "failure_reason": "Gloss and Re-solubility inferior"
          },
          {
            "test": "Ink base evaluation",
            "system": "Ink Base – Nitrocellulose Polyurethane, Finalux 108, Violet 27",
            "conditions": "Viscosity measured as B4 Cup @26°C; Gloss @ 60°; Re-solubility tested in Ethyl Acetate + Toluene (50:50)",
            "result": "Grinding (µm): < 5 µm (Ref Standard < 5 µm); Colour Shade: As per Std (Ref Standard); Transparency: Opaque (Ref Standard); Color Strength (%): 100.00 (Ref Standard 100.00); Viscosity (B4 Cup @26°C): 20 s (Ref Standard 19 s); Adhesion (Tape Test): Pass (Ref Standard Pass); Gloss @ 60°: 8.1 (Ref Standard 7.8); Re-solubility (Rating): 2 (Ref Standard 4); Separation: No (Ref Standard No); Settling: No (Ref Standard No)",
            "vs_reference": "Re-solubility inferior to BYK 9076",
            "verdict": "not ok",
            "failure_reason": "Gloss and Re-solubility inferior"
          }
        ],
        "sample_id": "unspecified sample"
      }
    ],
    "notes": "Rating scale: 1 – Fail, 2 – Poor, 3 – Average, 4 – Good, 5 – Excellent. Report header row for Colour of sample shows Ref Standard Amber / Batch Amber. Includes Re-solubility photographs (image3.jpeg, image2.jpeg). Project No and Issued by fields left blank in source.",
    "conclusion": "Results: Not OK (Gloss and Re-solubility inferior).",
    "outcome": {
      "status": "not ok",
      "basis": "Results: Not OK (Gloss and Re-solubility inferior).",
      "citation": "[S 9076 #63 not ok.docx, section \"Results\"]"
    }
  },
  "field_confidence": {
    "date": "high",
    "scientist": "high",
    "aim": "medium",
    "samples": "high",
    "conclusion": "high",
    "outcome": "high",
    "notes": "high"
  }
}